Lead-free elastomeric PVC/NBR insulation compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin and nitrile-butadiene rubberas the basic raw material, and add special plasticizer, stabilizer, flame retardant and other accessory ingredients.
環保型聚氯乙烯/丁腈復合物彈性體絕緣料是以優質聚氯乙烯樹脂和丁腈橡膠為基料，加入特種增塑劑、穩定劑、阻燃劑等助劑，經混合、塑化、造粒而成的粒狀電纜料。
 
Characteristics and Application 特點及用途
These products have good oil-resistant property, soft and flexible, and good processability. They can meet RoHS Standard. They are mainly used for the insulation of oil-resistant cables, elevator cables, oil-resistant soft wires of dust cleaner, heavy soft cables and crane cables.
產品具有良好的耐油性、彈性和柔軟性，加工性能優異，符合RoHS環保標準。主要用于有耐油要求的電線電纜、電梯電纜、耐油吸塵器軟線、重型軟線、起重機電纜等絕緣材料。
 
Processing Indicator加工工藝
Recommend to use of single-screw extruders with L/D= 20-25.
建議使用普通長徑比為20-25的單螺桿擠出機進行生產。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temperature 機頭溫度
W-7082 / W-9082 / W-0582	145-170℃	165-175℃

Physical and Electrical Properties
機械物理性能及電性能指標

Item 試驗項目		Unit 單位	Technical Requirements 技術要求
			W-7082	W-9082	W-0582
Density 比重		\	≤1.40	≤1.40	≤1.40
Tensile Strength 拉伸強度		MPa	≥12.5	≥12.5	≥12.5
Elongation at Break 斷裂伸長率		%	≥180	≥180	≥180
Thermal Aging 熱老化試驗		\	80℃×168h	100℃×240h	135℃×168h
Tensile Strength Variation 拉伸強度變化率		%	±40	±40	±40
Elongation Variation 斷裂伸長率變化率		%	±40	±40	±40
Dielectric Strength 介電強度		MV/m	≥20	≥20	≥20
200℃Thermal Stability 200℃時熱穩定時間		min	≥80	≥120	≥120
20℃Volume Resistivity 20℃時體積電阻率		Ω.m	≥1×1011	≥1×1011	≥1×1011
Brittle Temperature with Impact 沖擊脆化溫度		℃	-30	-30	-30
Oil Resistance 耐油性能(ASTM 902)	Temperature of Test試驗溫度	℃	70	100	100
	Time of Test 試驗時間	h	24	24	24
	Tensile Strength Variation 拉伸強度變化率	%	±40	±40	±40
	Elongation Variation 斷裂伸長率變化率	%	±40	±40	±40
Hardness 硬度		Shore A	≤75	≤75	≤75