Product Description產品描述
Lead-freeUV-resistant PVC jacketing compound are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
環保型聚氯乙烯抗紫外線護套料是以優質聚氯乙烯樹脂為基料，加入特種增塑劑、特種穩定劑等助劑，經混合、塑化、造粒而成的粒狀電纜料。
 
Characteristics and Application 特點及用途
The products have excellent climate-resistant property and good processability. They can meet RoHS Standard. All their properties are referred to GB/T 8815 and UL 1581 and other standards. They are mainly used for the jacketing of cables which have UV-resistant property requirements.
產品具有良好的耐候性，加工性能優異，符合RoHS環保標準。產品性能參考GB/T 8815、UL1581等標準的要求，主要用于有抗紫外線要求的電線電纜護套。
 
Processing Indicator加工工藝
Recommend to use single-screw extruders with L/D= 20-25.
建議使用普通長徑比為20-25的單螺桿擠出機進行生產。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temperature 機頭溫度
W-7021-Z / W-9021-Z / W-0521-Z	145-170℃	165-180℃

Physical and Electrical Properties
機械物理性能及電性能指標

Item 試驗項目	Unit 單位	Technical Requirements 技術要求
		W-7021-Z	W-9021-Z	W-0521-Z
Tensile Strength 拉伸強度	MPa	≥15.0	≥16.0	≥16.0
Elongation at Break 斷裂伸長率	%	≥180	≥180	≥180
Thermaldeformation 熱變形	%	≤50	≤40	≤40
Brittle Temperature with Impact 沖擊脆化溫度	℃	-25	-20	-20
200℃Thermal Stability 200℃時熱穩定時間	min	≥50	≥80	≥80
20℃Volume Resistivity 20℃時體積電阻率	Ω.m	≥1.0×108	≥1.0×109	≥1.0×109
Dielectric Strength 介電強度	MV/m	≥18	≥18	≥18
Thermal Aging 熱老化試驗	\	100℃×168h	100℃×240h	135℃×168h
Tensile strength after aging 老化后拉伸強度	MPa	≥15.0	≥16.0	≥16.0
Tensile Strength Variation 拉伸強度變化率	%	±20	±20	±20
Elongation After Aging 老化后斷裂伸長率	%	≥180	≥180	≥180
Elongation Variation 斷裂伸長率變化率	%	±20	±20	±20
Loss of Mass 質量損失(100℃×168h)	g/m2	≤23	≤15	≤20
Artificial weathering test 人工氣候老化試驗	\	720h
Tensile Strength Variation 拉伸強度變化率	%	±20	±20	±20
Elongation Variation 斷裂伸長率變化率	%	±20	±20	±20